Chemistry: Low Temperature Hydrothermal Synthesis of Cu-Nd Doped Zinc Oxide Nanorods

 

Low Temperature Hydrothermal Synthesis of Cu-Nd Doped Zinc Oxide Nanorods

Ghazi M. Abed1*, Basim I. Al-Abdaly 2, Abdulkareem M. A. Alsammarraie2

1Ministry of Science and Technology, Baghdad, Iraq

2Department of Chemistry, College of Science, Baghdad University, Baghdad, Iraq

Abstract

Cu-Nd doped ZnO nanorods were grown hydrothermally at 90C on quartz substrate previously spin coated with self-assembly deposited ZnO nanoparticles.

The products were extensively examined by XRD, SEM, AFM, Raman and Uv-Vis techniques. The results revealed that the formed nanorods have hexagonal wurtzite structure with a diameter between 100 to 200 nm and 1-3 µm in length, the calculated optical energy gap was (3. 15 eV).

Keywords: Cu-Nd doped ZnO, nanorods, hydrothermal, self-assembly.

تحضير العصي النانوية لاوكسيد الزنك المشوب بالنحاس والنيوديميوم بطريقة

التعامل الحراري المنخفض الرطب

غازي محمد عبد1*, باسم ابراهيم العبدلي2, عبدالكريم محمد علي السامرائي2

1وزارة العلوم والتكنلوجيا، بغداد، العراق

2قسم الكيمياء، كلية العلوم، جامعة بغداد، بغداد, العراق

الخلاصة:

تم تحضير العصي النانويه لاوكسيد الزنك المشوبة بالنحاس – نيوديميوم بالتعامل الحراري الرطب بدرجة 90 م على الواح من زجاج الكواتز المطلية مسبقا بدقائق اوكسيد الزنك المحضرة بالنمو الذاتي.

جرى الفحص بواسطة تقنيات حيود الاشعة السينية و المجهر الالكتروني الماسح و مجهر القوه الذرية و طيف رامان و الاشعة فوق البنفسجية و المرئية وبينت النتائج ان العصي النانوية المتكونة ذات طور بلوري فورتزايت سداسي و باقطار ترواحت بين 100 الى 200 نانو متر وباطوال مقاربة لـ 1-3 مايكرومتر اما حاجز الطاقة البصرية المحسوبة فقد بلغت 3.15 الكترون فولت.