Physics: STRUCTURE, AC CONDUCTIVITY AND POWER LOSS IN PVC AND PMMA POLYMERS

 

Structure, AC Conductivity and Power Loss in PVC and PMMA Polymers

Hameed M. Ahmed and Shuja-Aldeen B. Aziz

Department of Physics, College of Science-Sulaimani University, Sulaimani – Iraq.

Abstract

     Frequency and temperature dependence of AC-conductivity () and power loss () for polyvinyl chloride (PVC) and poly (methyl methacrylate) (PMMA) were studied (in the frequency range 1KHz-1MHz and in the temperature range 20-100°C). It has been found that the AC-conductivity increases with increasing frequency and temperature for both samples. The value of the exponent is less than 1 for both samples as determined experimentally. The power loss which is in the form of heat, is increased for both samples with increasing frequency and temperature. The IR spectra shows the presence of C-Cl and C=O bond, which are the main sources for power loss.

 

 

التركيب والتوصيلية المتناوبة و فقد القدرة للبوليمرين .PMMA ,PVC   

حميد مجيد أحمد و شجاع الدين بكر عزيز

قسم الفيزياء، كلية العلوم، جامعة السليمانية ، السيليمانية – العراق.

الخلاصة

تم دراسة تأثير التردد و درجة الحرارة على التوصيلية المتناوبة() و فقد القدرة () لمادة بولي ميثاكريلايت المثيلPMMA وكذلك مادة بولي كلورايد الفاينايل PVC لمدى من التردد 1 كيلو هرتز الى 1 ميكا هرتز ودرجة حرارة من 20 الى 100 درجة مئوية. من خلال الدراسة تبين ان التوصيلية المتناوبة تزداد بزيادة التردد ودرجة الحرارة لكلا المادتين.لقد وجدت قيمة الاكسبونينت (S) اقل من واحد لكلا المادتين من خلال التجربة.اما فقد القدرة والتى هى بشكل حرارة تزداد بزيادة التردد ودرجة الحرارة.لقد اظهرت دراسة الاشعه تحت الحمراء الاواصر (C-Cl) و (C=O) والتى تعتبر المصدر الرئيسى لفقد القدرة.